4,4{40 -Stilbenebis-pyridooxazoles and related optical brighteners and polymeric compositions brightened thereby

ABSTRACT

4,4&#39;&#39;-Stilbenebis-2-oxazolopyridines, -2-thiazolopyridines, and 2-imidazopyridines are optical brightening agents useful for whitening and brightening natural and synthetic fibers, papers, resins and the like. The compounds are conveniently prepared by interacting 4,4&#39;&#39;-stilbenedicarboxylic acid or its acid chloride with a vicinal disubstituted pyridine compound consisting of vicaminohydroxypyridine, vic-aminomercaptopyridine or vicdiaminopyridine, respectively.

United States Patent [:91

Crounse 4,4 '-S'I'lLBENEBIS-PYRIDOOXAZOLES AND RELATED OPTICAL BRIGHTENERS AND POLYMERIC COMPOSITIONS BRIGHTENED TI-IEREBY [75] Inventor: Nathan N. Croume, Cincinnati,

Ohio

[73] Assignee: Sterling Drug Inc., New York, NY.

[22] Filed: Apr. 28, 1969 [2|] Appl. No.: 820,005

OTHER PUBLICATIONS Chemical Abstracts, Vol. 73, Abst. No. ll90l2 [4 1 Dec. 23, 1975 Chemical Abstracts, Vol. 75, Abst. No. 99260t (I971).

Primary Examiner-John D. Randolph Attorney, Agent, or Firm-Lynn T. Fletcher; B. Woodrow Wyatt [5 7] ABSTRACT 4,4-Stilbenebis-2-oxazolopyridines-2-thiazolopyridines, and 2-imidazopyridines are optical brightening agents useful for whitening and brightening natural and synthetic fibers. papers. resins and the like. The compounds are conveniently prepared by ini like. The compounds are conveniently prepared by interacting 4,4'-stilbenedicarboxylic acid or its acid chloride with a vicinal disubstituted pyridine compound consisting of vic-aminohydroxypyridine, vicaminomercaptopyridine or vic-diaminopyridine, respectively.

3 Claims, No Drawings 4,4'-STlLBENEBlS-PYRIDOOXAZOLES AND RELATED OPTICAL BRIGHTENERS AND POLYMERIC COMPOSITIONS BRIGHTENED THEREBY This invention relates to novel compositions of matter classified in the art of chemistry as heterocyelicsubstituted stilbenes and to methods for preparing them. More particularly the invention relates to novel oxazolopyridinyl, thiazolopyridinyl and imidazolopyridinyl derivatives of stilbene useful as optical whitening and brightening agents for natural and synthetic fibers, papers-resins, and the like.

In its composition aspect the present invention resides in the concept of novel chemical compounds having the general structural formula wherein Py, and Py are each a bivalent heterocyclic nucleus of the pyridine class in which the open bonds are on vicinal ring carbon atoms of said nucleus; and X, and' X are each a member of the class consisting of O, S and NR, wherein R is a member of the group consisting of H, lower alkyl, hydroxy-lower alkyl, hydroxyoxaalkyl, phenyl-lower alkyl, eyano-lower alkyl, carboxylower alkyl, carbo-lower alkoxy-lower alkyl, phenylhydroxy-lower alkyl and lower alkenyl, and A is a bivalent 4,4'-stilbene radical. in accordance with this aspect of the invention, attached at the 4 and 4'-positions of stilbene radical, my new compounds have the same or different heterocyclic radical selected from the following class: 2-oxazolo[5,4-b]pyridyl, 2-oxazolo[5,4-

clpyridyl, 2-oxazolo[4,5-b]pyridyl, 2-oxazolo[ 4,5- c ]pyridyl, 2-thiazolo-[ 5 ,4b lpyridyl, 2-thiazol0[ 5 ,4- e ]pyridyl, 2-thiazolo[4,5-blpyridyl, 2-thiazolo[4,5

c]pyridyl, 2-imidazo[4,S-b]pyridyl, and 2-imidazo[4,5- clpyridyl. Compounds of this class have been found to have unexpectedly superior fluroscent properites when used as whitening and brightening agents and, in addition, have high stability to heat, light, chlorinetype bleaches, and resin-finish catalysts, which make them particularly useful for whitening and brightening textile materials.

ln Formula l above Py and Py, are each a heteroeyclic nucleus of the pyridine class. Thus, Py and Py, can be the same or different and are selected from the class consisting of pyridine and pyridine substituted by one or more monovalent substituents which tend to increase the solubility of the resulting compound in syn thetic resins and fibers. Such substituents inelude 'iH, lower alkyl and halogen; that is, chlorine, bromine, iodine and fluorine. The aforementioned substituents have the advantage of increasing solubility in synthetic resins without, however, tending to impart color to the resulting compound; that is, they are not auxochromic substituents. The compounds of my invention are strongly fluorescent and are used as optical whitening and brightening agents in high dilution. Therefore they may have slight color without impairing the overall whitening effect. However, auxochromic substituents tend to impart too much color to the compound and thus lessen its value as a whitening agent.

ln Formula I above X, and X are members of the class consisting of O. S. and NR. When X or X. is NR,

R is H; lower alkyl; preferably containing from I to 6 carbon atoms; hydroxy-lower alkyl, preferably containing from 2 to 6 carbon atoms; hydroxyoxaalkyl, preferably containing from 3 to 15 carbon atoms; phenyllower alkyl, preferably containing from 7. to l l carbon atoms; cyano-lower alkyl, preferably containing from 3 to 6 carbon atoms; carboxy-lower alkyl, preferably containing from 2 to 6 carbon atoms; carbo-lower alkoxy-lower alkyl, preferably containing a total of from 3 to l2 carbon atoms; phenylhydroxy-lower alkyl, preferably Containing from 8 to l l carbon atoms; or lower alkenyl, preferably containing from 3 to 6 carbon atoms.

When R is lower alkyl there are included, for example, methyl, ethyl, n-propyl, isopropyl, n-butyl. isoamyl, n-hexyl, and the like. When R is hydroxy-lower alkyl, there are included, for example Z-hydroxyethyl, 2- hydroxypropyl, 2,3-dihydroxypropyl, and the like. When R is hydroxyoxaalkyl there are included, for example, 2-hydroxy-3-(2,3-dihydroxypropoxy propyl, 2-hydroxy-3-(2-hydroxyethoxy)propyl, Z-hydroxy- 3 [2-(2hydroxyethoxy)ethoxylpropyl, and the like. When R is phenyl-lower alkyl there are included, for example, benzyl, phenethyl, 3-phenylpropyl, 3-phenyl' pentyl, and the like. When R is cyano-lower alkyl there are included, for example, 2-eyanoethyl, 3-cyanopropyl, 4-cyanopentyl, and the like. When R is carboxy-lower alkyl there are included, for example, earboxymethyl, Z-earboxyethyl, 3- carboxypropyl, 5- carboxypentyl, and the like. When R is carbo-lower alkoxy-lower alkyl there are included, for example, carbomethoxymethyl, Z-carbomethoxyethyl, 2-carbobutoxyethyl, 3-carbohexyloxypropyl, S-earbomethoxypentyl, and the like. When R is phenylhydroxylower alkyl there are included, for example, B-phenyl- B-hydroxyethyl, aphenyl-B-hydroxyethyl, B-phenyl-B- hydroxypropyl, and the like. When R is lower alkenyl there are included, for example, allyl, methallyl, 3,3- dimethylallyl, and the like.

In Formula I above, A is a bivalent 4,4'-stilbene radical of the formula wherein the substituents represented by the term Z are the same or different monovalent substituents bound to the benzene ring by a covalent bond. Z can be any such substituent which does not destroy the desirable fluorescent properties of the compound as a whole. Typical examples of such substituents represented by Z are H; halogen i.e., chlorine, bromine, iodine and fluorine; lower alkyl, as defined above, for example. methyl. ethyl, propyl, n-butyl, tert-butyl, amyl, secxamyl and hexyl; lower alkoxy, for example. methoxy, ethoxy, propoxy, isopropoxy, hexyloxy and the like; aryloxy, wherein the aryl moiety is a oneor two-ring carbocyclic aromatic radical, for example, phenoxy, naphthyloxy. ochlorophenoxy, and the like; lower alkanesullonyl wherein the lower alkane moiety contains from one to about six carbon atoms, for example, me-

thanesulfonyl, ehtanesulfonyl, butanesulfonyl, and hexanesulfonyl, arenesulfonyl wherein the arene moiety is a oneor two-ring carbocyclic aromatic radical, for example, benzenesulfonyl, p-toluenesulfonyl, B-naphthalenesulfonyl, and the like; sulfamyl; N-substituted sulfamyl, for example, N,N-dimethylsulfamyl, N-ethylsulfamyl, N-phenylsulfamyl and the like; cyano; carbamyl, and N-substituted carbamyl, for example, N,N- dimethylcarbamyl, N,N-dibutylcarbamyl, N-phenyl-N- methylcarbamyl, N-(2-napthylcarbamyl) and the like.

The substituents represented by the term Y are the same or different monovalent substituents selected from the group consisting of H; alkyl of from 1 to 18 carbon atoms, for example methyl, ethyl, n-butyl, isobutyl, 2-ethylhexyl, n-pentyl, n-decyl, n-dodecyl, and cetyl; and cyano.

Normally no more than one or two of the substituents Y and 2 above are other than H, because the simpler 4,4'-stilbene-disubstituted compounds are cheaper and more easily prepared and are as good or better fluorescent brightening agents than the more highly substituted compounds.

In another of its aspects, the present invention resides in the concept of a process for preparing the compounds depicted in Formula l which comprises interacting a 4,4'-stilbenedicarboxylic acid compound with a vicinal-disubstituted pyridine compound consisting of a vic-aminohydroxypyridine (vic-aminopyridino), a vic-aminomercaptopyridine (vic-aminopyridinethiol) or a vic-diaminopyridine compound. The reaction takes place by heating said reactants under conditions conducive to the elimination of four molecular equivalents of water. Two reactions are involved in this process, the first being the formation of a 4,4'-stilbenebis-- carboxamide intermediate, and the second being a cyclization of the intermediate to the final heterocylic compound. The process can be carried out in such a manner that the intermediate carboxamide is isolated, or, if desired, the cyclization reaction can be carried out directly without isolation of the intermediate.

In still another of its aspects, the present invention resides in the concept of a process for preparing the compounds depicted in Formula I which comprises interacting a 4,4'-stilbenedicarbonyl chloride compound with a vicinal'disubstituted pyridine compound consisting of a vic-aminohydroxypyridine, a vicm 4,4'-stilbenebiscarboxamide or, if desired, the cyclization can be carried out directly without isolation of the intermediate.

In general, the compounds of the above structure are high melting yellow to yellow-green solids which have the following solubility characeristics. They are insoluble in water, hydrocarbons, halogenated aliphatic hydrocarbons, ketones, ethers and the lower aliphatic alcohols. They are generally slightly soluble in hot dimethylformamide, benzyl alcohol and the higher boiling halogenated hydrocarbons such as trichlorobenzene and chlorinated biphenyl. They are moderately soluble in some mineral acids, for example cold sulfuric acid and hot polyphosphoric acid, but they are usually precipitated in their acid addition salt form when the acid solution is diluted with water. The compounds wherein X, or X,, or both, are NH are generally soluble in alcoholic alkali metal hydroxides, amides, and alkoxides, presumably due to the formation of the soluble alkali metal salt form.

A preferred class of compounds of this invention comprise compounds of the structure of Formula ll was:

Fo rmula II wherein each of R,, R and R is a member of the class consisting of H, halogen, lower alkoxy and lower alkyl,

and X and X: are as defined above in Formula I.

A particularly preferred class of compounds of the invention are the oxazolopyridines of Formula I wherein X, and X are each 0. These compounds are 5 preferred because of their superior fluroescence and Formula III which possesses an unusually high degree of fluorescence under ultraviolet light at a wavelength of maxi mum emmision of 440 nm when dispersed in polyethylene terephthalate. Moreover this compound is unusu- 3 ally stable to the effects of heat and light, and is thus well adapted for incorporation into textile fiber spinning melts.

Characteristic of compounds containing a pyridine ring, the compounds of this invention react with mild oxidizing agents and with alkylating agents with the formation. respectively, of N-oxides and quaternary ammonium salts. These compounds tend to be somewhat more soluble in polar solvents than their respective parent compounds. Although the fluorescence of these compounds is somewhat weaker than that of the parent amines, the N-oxides and quaternary ammonium salts are useful brightening agents which are effective for the purposes described above.

The manner and process of making and using my invention will now be described so as to enable any person skilled in the art to which it pertains to make and use the same, as follows:

The novel fluorescent compounds of my invention can be prepared by any of several methods. One such process comprises heating 4,4'-stilbenedicarboxvlic acid chloride (4,4'-stilbenedicarbonyl chloride) with an aminopyridine compound which has in a position vicinal to the amino group an hydroxyl, mercapto or amino group. whereupon there is formed, respectively, N ,N '-bis(orthohydroxypridyl-4,4 '-stilbenedicarboxamide or N ,N -bis(orthoaminopyridyl)-4,4 stilbene dicarboxamide. The reaction is carried out by heating the reactants in a suitable inert solvent, for example. toluene, chlorobenzene, dioxane, benzene, xylene and the like. As will be obvious to one skilled in the art, this type of reaction proceeds under a wide variety of conditions. We prefer to reflux the reactants in a solvent such as that described above with or without the addition of an acid acceptor. Of course, the reactant itself can serve as an acid acceptor inasmuch as the pyridine compound is basic. The reaction is usually complete in four to eight hours. The resulting pyridylstilbenedicarboxamide compound is cyclized with or without isolation by heating it to a temperature of l7S250C. in a high boiling solvent, for example, trichlorobenzene, mineral oil, quinoline, or a eutectic mixture ofdiphenyl ether and biphenyl, in the presence of a strong acid, for example, p-toluene sulfonic acid. Alternatively. the pyridylstilbenedicarboxamide compound can be cyclized by heating the compound in polyphosphoric acid at about 200 C. It is convenient to follow the progress ofthe cyclization reaction by means of the ultraviolet absorption spectra of small samples of the reaction mixture taken during the course of the reaction. Because the cyclization results in the formation of a new heteroaromatic ring, the ultraviolet absorption changes perceptibly as the reaction proceeds. The reaction is deemed complete when the spectra of two consecutive samples are the same.

In accordance with this invention, the compounds of Formula l can also be prepared in one step by heating stilbenedicarboxylic acid with a vicinal substituted aminopyridine compound mentioned above in polyphosphoric acid, whereupon condensation and cyclization occur simultaneously. The reaction is carried out by rapidly stirring the reactants while they are heated to a temperature of l25 to 225 C. for approximately 4 to 8 hours. The product is isolated by pouring the reaction mixture into a large excess of ice and water, neutralizing the excess acid, and collecting the precipitate in conventional fashion.

In accordance with another process for preparing the compounds of my invention. o'aminohydroxypyridine, o-aminomercaptopyridine, or o-diaminopyridine is heated with p-toluic acid in polyphosphoric acid at approximately 225-275 C. for 48 hours to provide, respectively, a 2-p-tolyloxazolopyridine, 2-p-tolythiazolopyridine or 2-p-tolylimidazopyridine. These latter compounds are conveniently converted into corresponding stilbene compounds by the conventional sulfur melt" method described in the prior art, which comprises heating the tolylsubstituted reactant in molten sulfur at about 250 C. for approximately 6-8 hours.

The preferred compound of Formula lll can be prepared in accordance with still another process, as follows. By condensing 3-amino-2chloropyridine instead of 3-amino-2-pyridinol with 4,4'-stilbenedicarbonyl chloride under the conditions described above, there is obtained the intermediate N,N'-bis(2-chloro-3- pyridyl)-4,4'stilbenedicarboxamide. This compound is conveniently cyclized to 4,4-stilbenebis(2- oxoazolo{5,4-b]pyridine) by heating it at approximately 15 8-200 C. with two molecular equivalents of a copper (II) salt and an amine in an inert solventv Depending upon the temperature the reaction is usually complete in approximately four to eight hours. The nature of the copper (II) salt is not critical; for example, cupric chloride, cupric sulfate, or cupric acetate may be used, but i have found cupric acetate to be convenient for economical reasons. Pyridine is the most convenient amine, but ammonia or alkyl-substituted amine can also be used. Suitable inert solvents include nitrobenzene, o-dichlorobenzene, tirchlorobenzene, naphthalene, and dimethylformamide.

The 4,4'-stilbenebis(2-imidazo[4,5-b]pyridine) and 4,4'-stilbenebis (2-imidazol4,5-c]pyridine) prepared in accordance with the general procedures described above react readily with alkylating agents to yield N- mono and N.N'-di (alkyl or substituted alkyl) derivatives which are useful whitening and brightening agents of Formula 1 wherein X and X are NR and R is alkyl or substituted alkyl radical of the type hereinabove described. The alkylation reaction is readily carried out by heating 4,4'-stilbenebis (2-imidazo[4,5b]pyridine) or 4,4-stilbenebis(2-imidazo[4,5-clpyridine) (Formula I wherein X and X are each NH) with the appropriate alkylating agent. Usually a heating period of about 2 to 6 hours at 5()l 50 C. is sufficient to produce a satisfactory yield of the desired product. Alkylating agents useful for this reaction include, for example. esters of strong organic and inorganic acids having the formula R-An wherein R is a member of the class consisting of lower alkyl, hydroxy-lower alkyl, hydroxyoxaalkyl, phenyl-lower alkyl, cyano-lower alkyl, carboxy-lower alkyl, carbo-lower alkoxy-lower alkyl, phenyl-hydroxy-lower alkyl and lower alkenyl radicals and An is the anion of the strong acid. illustrative of these esters are methyl sulfate, ethyl sulfate, methyl p-toluenesulfonate; lower alkyl halides, for example, methyl iodine, ethyl bromide, butyl bromide, and hexyl chloride; phenyl-lower alkyl halides, for example benzyl chloride, p-chlorobenzyl chloride, 2-chloro-4- methoxybenzyl chloride, and benzyl bromide; allyl and methallyl halides, for example, allyl bromide and meth allyl chloride; carboxy-lower alkyl halides. for example chloroacetic acid, 3-chloro propionic acid, Z-bromopropionic acid, cyano-lower alkyl halides, for example, chloroacetonitrile and 3-bromopropionitrile; hydroxylower alkyl halides, for example 2,3dihydroxypropyl chloride, ethylene chlorohydrin, ethylene bromohydrin, and isobutylene chlorohydrin; hydroxyoxaalkyl halides, for example, 2-hydroxy-3-(2,3-dihydroxypropoxy)propyl chloride and 2-hydroxy2-[3-(2- hydroxyethoxy) ethoxy1propyl chloride; carbo-lower alkoxy-lower allyl halides, for example, methyl bromoacetate, ethyl 3chloropropionate and butyl chloroac etate. Also useful as alkylating agents are lower alkylene oxides, for example, ethylene oxide, propylene oxide and epichlorohydrin; styrene oxide; p-chlorostyrene oxide; acrylonitrile; methacrylonitrile; and ethyl acrylate.

The N-monoalkylated compounds (Formula I where only one of X and X is NH) are obtained by heating preferably one or advantageously slightly more than one molecular equivalent of the appropriate alkylating agent with one molecular equivalent of the 4,4'-stilbenebis(l-imidazopyridine). Minor proportions of the corresponding N,Ndialkylated compound (Formula I, where neither of X and X is NH) and of unreacted N,N'-unsubstituted starting material varying in amounts depending in part on the relative proportions of the reactants and in part on the reaction conditions, will be found associated with the N-monoalkylated compound obtained as the chief product of the alkylation reaction. If desired, the N-monoalkylated product can be purified, for example by use of suitable solvents, but ordinarily it is unnecessary and uneconomical for practical purposes to effect such purification since the mixture is directly useful as a whitening and brighten ing agent.

As will be understood, the use of larger proportions of the alkylating agent favors higher yields of the N,N')\ dialkylated compound. When this is the desired product, there are, of course, required by theory at least two molecular equivalents of the alkylating agent per equivalent of the 4,4'-stilbenebis(Z-imidazopyridine); as a matter of fact, for best conversion to the dialkylated product an excess of the alkylating agent should be employed, for example an excess of 1-4 equivalents of the alkylating agent. The N,N'-dialkylated compounds obtained in this manner are symmetrical. When an unsymmetrical product is desired, an N-monoalkylated compound or, alternatively, a reaction mixture containing it is treated with a different alkylating agent, thereby producing a compound of Formula 1 wherein X, and X contain different alkyl or substituted alkyl radicals.

When the alkylating agent has a hydroxyl group in its structure, for example, a hydroxy-lower alkyl or bydroxyoxaalkyl compound, the hydroxyl function in the resulting N-monoalkylated product (e.g., Formula I, X NH, X hydroxy-lower alkyl or hydroxy-oxaalkyl) interacts with a second equivalent of the same or a different alkylating agent to yield preferentailly O- alkylated products rather than the expected N,N'- dialkylated derivative, the latter being produced only in relatively small amount. The use of a large excess of the alkylating agent leads to substantially complete production of N,N'disubstituted products.

The compounds of my invention have been found to have high stability to heat and light and thus are well adapted for use as optical brightening agents by incorporation into melts of normally solid, fiber and filmforming polymeric material, for spinning synthetic fibers, or for casting or molding plastics in a concentration of from 0.005 to 0.5 per cent by weight of the polymeric material. A further method utilizing the compounds of my invention is to impregnate textile fabrics comprising synthetic fibers, for example, polyester (poly[terephthalic acid ethyleneglycol esterl) poly( 1,4-cyclohexylenedimethylene terephthalate, or nylon, with an aqueous dispersion compound at temperatures below about -l00 C., for example. at room temperature, and then to subject the treated fabric to a dry heat treatment at a temperature above l00 C. The fabric may advantageously be dried at temperatures in the range 25l00 C. prior to the heat treatment which is preferably carried out at temperatures in the range l25-250 C. Said heat treatment may be accomplished by any of several known methods, for example, by heating in a dry chamber, by ironing the fabric, or by treating it with dry, super-heated steam.

The structures of the new compounds of my invention were determined by their mode of synthesis and by the correspondence of calculated and found values of elemental analyses of representative samples, and were corroborated by ultraviolet and infrared spectroanalyses.

The best mode contemplated for carrying out my invention will now be set forth in the following examples, which are given for the purpose of illustration without limiting the invention thereto'.

EXAMPLE l 4,4"stilbenebis( 2-oxazolo[4,5c ]pyridine) To '75 g. of polyphosphoric acid preheated to 100 C. was added 5.5 g. (0.02 mole) of4,4' stilbenedicarboxylic acid. The mixture was then further heated to l25 C. and 5.9 g. (0.04 mole) of 3-amino-4-pyridinol hydro chloride was added in small portions over a period of fifteen minutes. When the addition was complete, the mixture was heated with stirring at about 200 C. for 3% hours. The resulting brown solution was poured into 375 ml. of water, and the misture was stirred until the product congealed; the latter was collected on a filter, washed with water, and dried at 70 C. in vacuo.

The impure 4,4-stilbenebis(2-oxazolo[4,5-c]pyri dine) thus prepared was purified as follows: The product was stirred with aqueous sodium hydroxide at pH 10 and at 95 C. for hour. The remaining solid product was collected on a filter and was washed free of alkali with water. The dried product was then recrystallized from trichlorobenzene to give 4,4'-stilbenebis(2-oxazolo[4,5-clpyridine) which melted at 345-360 C. with decomposition. The gram extinction coefficient at the wavelength of maximum absorption of a solution of this compound in dimethylformamide was 122.8 at 370 nm. This compound has the structural formula EXAMPLE 2A EXAMPLE 2B In accordance with another procedure for preparing 4.4-stilbenebis(2-oxazolo[5,4-b]pyridine) 8.5 ml. (0.163 mole) of thionyl chloride dissolved in ml. of chloroform was added dropwise to 11.5 g. (0.03 mole) of dipotassium 4,4'-stilbenedicarboxylate suspended in l50 ml. of dry chlorobenzene. The mixture was refluxed for 3 hours, and the excess thionyl chloride was removed by distillation. To the resulting solution of 4,4'-stilbenedicarbonyl chloride in chlorobenzene was added 8.57 g. (0.06 mole) of 3-amino2-chloropyridine in 50 ml. of dry chlorobenzene and 11.0 ml. of dry pyridine. The mixture was refluxed for 8.5 hours, and the solid product was collected on a filter and washed with chlorobenzene and with methanol. This intermediate, N,N-bis(2-chloro-3-pyridyl)-4,4'-stilbenedicarboxamide, was purified by washing it chloride ion-free with water, drying, and recrystallizing from hot tricholrobenzene. The melting point of this product was 29l293 C.

The above intermediate, N.N-bis(2-chloro-3- pyridyl)-4.4-stilbenedicarboxamide was cyclized to the desired 4,4'-stilbenebis(2-oxazolo[5.4,b]pyridine) as follows. To a solution containing 20 ml. of pyridine and 4.4 g. of cupric acetate monohydrate in 56 ml. of dimethylformamide was added 4.89 g. (0.0] mole) of N,N-bis(2-chloro-3-pyridyl)-4,4'-stilbenedicarboxamide. prepared as above. The mixture was refluxed under nitrogen for about 6 hours, and then about 35 ml. of the solvent was removed by distillation. The residue was allowed to cool and the solid product was 10 formamide solution of 4,4'-stilbenebis(2-oxazolo[5,4- blpyridine) thus prepared was 200.4 at 375 nm, its wavelength of maximum absorption.

When 4.16 g. (0.01 mole) of this product was refluxed in excess benzyl chloride in the presence of 2. l 2 g. of sodium carbonate there was obtained a quaternary ammonium salt having, in dimethylformamide solution, a gram extinction coefficient of 71.6 at 354 nm, the wavelength of maximum absorption.

EXAMPLE 3 To a suspension of 18.5 g. (0.05 mole) of dipotassium 4,4'-stilbenedicarboxylate in 250 ml. of dry chlorobenzene was added dropwise 13 ml. of thionyl chloride dissolved in 35 ml. of chlorobenzene. The mixture was refluxed for about three hours, and then 86 ml. of solvent was removed by distillation to remove all excess thionyl chloride. The the resulting solution of 4,4' stilbenedicarbonyl chloride in chlorobenzene at about C. was added [1.5 g. (0.01 mole) of 2-amino-3- pyridinol in 75 ml. of dry chlorobenzene and 9 ml. of

pyridine. This mixture was refluxed for 10 hours and was allowed to cool to room temperature. The interme diate N,N'-bis(3-hydroxy-2-pyridyl)4,4'-stilbenedicarboxamide hydrochloride was collected on a filter and was washed with chlorobenzene, methanol and water. The cake was then suspended in aqueous methanol and made alkaline with 10 per cent aqueous sodium carbonate solution. The resulting N,N'-bis(3-hydroxy-2- pyridyl)-4,4-stilbenedicarboxamide remained unmelted at 360 C. This intermediate product was ringclosed to 4,4"stilbenebis( 2oxazolo[4,S-b]pyridine) by heating 9.0 g. of the dry product in ml. oftrichlorobenzene containing 9.6 g. of p-toluenesulfonic acid at 200-2l0 C. for about 19 hours. The mixture was poured into water. neutralized, and collected on a filter. The product was purified by recrystallization from methanolic phenol. It was then poured into dilute aqueous sodium hydroxide, collected on a filter, and washed alkali-free with water. The 4,4"stilbenebis(2 oxazolo[4,5-b]pyridine) thus obtained remained unmelted at 300 The gram extinciton coefficient of this compound in dimethylformamide solution was 180.6 at 377 nm, the wavelength of maximum absorption. The compound has the structural formula collected on a filter. It was triturated with concentrated hydrochloric acid to decompose and dissolve any copper complex, and it was then collected on a filter, washed free of acid with water, and dried under vacuum. The gram extinction coefficient of a dimethyl- EXAMPLE 4 When 3-amino-4-pyridinethiol is substituted for 3- amino-4-pyridinol in Example 1 hereinahove there is obtained 4,4-stilbenebis(2-thiazolo[4,5-c]pyridine). This compound has the structural formula EXAMPLE 5 Following a procedure similar to that described above in Example I, but using 4-amino-3-pyridinethiol instead of 3-amino4pyridinol there is obtained 4,4- stilbenebis( 2 thiazolo[5,4-c]pyridine). This compound has the structural formula Following a procedure similar to that described above in Example I except that 2-amino-6-methyl pyridinethiol is used in place of 3-amino-4-pyridinol there is obtained 4,4'-stilbenebis(5-methyl-2- thiazolol4 5-b]pyridine), having the structural formula The intermediate 2-amino-6-methylpyridine is prepared as follows: To a solution of 68 g. (0.63 mole) of 2-amino-6-methylpyrindine in about 500 ml. of glacial acetic acid cooled to l-l 5 C., is added a mixture of [70.2 g. (2.1 moles) of sodium thiocyanate suspended in about 570 ml. of glacial acetic acid. A solution containing 30.5 ml. of bromine in about 60 ml. of glacial acetic acid is the added, and the mixture is stirred at l()l 5 C. for 1 hour and then at 7580 C. for /&hour. The solution is filtered. and the solvent is removed from the filtrate under reduced pressure. The residue is recrystallized from isopropyl alcohol containing activated charcoal. The 2-amino-5-methylthiazolo[4,5- blpyridine thus obtained melts at l50l60 C. The product is hydrolyzed by refluxing 8 g. of the material in 120 ml. of the 20 percent aqueous sodium hydroxide solution for 6 hours. The resulting cloudy solution is filtered. and the filtrate is acidified and reduced to dryness. The residue is extracted with hot ligroin to yield 2-amino-o-methyl-3-pyridinethiol. melting at l 33-l 38 C.

EXAMPLE 7 When 3-amino-2-pyridinethiol is substituted for 3 amino-4-pyridinol in Example 1 hereinabove there is obtained 4.4-stilbenebis(2-thiazolo[5,4-blpyridine), having the structural formula C2H5 l EXAMPLE 8 Following a procedure similar to that described above in Example 3 but using 3-amino-6-chloro-2- pyridinethiol instead of 2-amino-3-pyridinol there is obtained 4 4'-stilbenebis( 5-chloro-2-thiazolo[ 5 ,4- blpyridine), having the structural formula EXAMPLE 9 Following a procedure similar to that described above in Example 1 except that 3-amino-5-ethoxy-2- pyridinethiol is used in place of 3-amino-4-pyridinol there is obtained 4,4'-stilbenebis(6-ethoxy-2- 35 thiazolol 5,4-blpyridine), having the structural formula C/EnOC I-IS l EXAMPLE l0 o on o n s EXAMPLE ll Following a procedure similar to that described above in Example I but using 3-amino-5-chloro-2- pyridinethiol instead of 3-amino-4-pyridinol there is obtained 4,4'-stilbenebis(6-chloro'2-thiazolo[5,4- b]pyridine). having the structural formula c cu- EXAMPLEIZ Following a procedure similar to that described above in Example 3 except that 3-amino-6-ethoxy-2- pyridinethiol is used in place of 2-amino-3-pyridinol there is obtained 4,4'-stilbenebis(5-ethoxy-2- thiazolol 5,4-blpyridine), having the structural formula cac a o N EXAMPLE 13 When 3-amino-5-bromo-4-pyridinethiol is substituted for 3-amino-4-pyridinol in Example l hereinabove there is obtained 4,4'-stilbenebis(7-bromo-2- thiazolo{4,5-c]pyridine), having the structural formula instead of 3-amino-4-pyridinol there is obtained 4.4- stilbenebis(2-oxazolo[5,4-clpyridine), having the structural formula Q in CH I hlpyridine), having the structural formula EXAMPLE [5 Following a procedure similar to that described above in Example 1 except that 3-amino-5-bromo-2- pyridinol is used in place of 3-amino-4-pyridinol there is obtained 4,4'-stilbenebis((rbromo-Z-oxazololS,4- b]pyridine) having the structural formula l C CH- N I CH EXAMPLE 16 When 3-amino-S-chloro-2pyridinol is sutstituted for 3-amino-4-pyridinol in Example I hereinabove there is 35 obtained 4,4'-stilbenebis(6-chloro-2-oxazolol5 4- b]pyridine) having the structural formula /N C1 Qw EXAMPLE 1? Following a procedure similar to that described above in Example 1 except that 3-amino-5-methyl-2 pyridinol is used in place of 3-amino-4-pyridinol there is obtained 4.4'-stilbenebis(6-methyl-2-oxazolol5,4-

C 0 CH3 ture was refluxed for 3 hours and about half of the solvent was removed by distillation to remove all traces of excess thionyl chloride. The resulting solution of 4,4'-stilbenedicarbonyl chloride in chlorobenzene was cooled to 65 C., and ll.4 g. (0.105 mole) of 2,3- diaminopyridine was added portionwise, followed by 9 ml. (0.1 mole) of pyridine in 75 ml. of dry chlorobenzene. The mixture was heated to reflux whereupon an exothermic reaction started; reflux was continued for 10 hours. After cooling the mixture, the product was collected on a filter and washed thoroughly with chlo' robenzene and methanol. The product was then triturated with sodium carbonate solution, washed free of chloride ion withdistilled water, and dried. The resulting N,N'-bis( 3-amino-2-pyridyl )-4,4'-stilbenedicarboxamide remained unmelted at 310 C. Infrared spectral analysis of the product showed a strong band at 1645 cm, indicative of the presence of an amide carbonyl. The ultraviolet absorption spectrum showed maxima at 36l and 377 nm.

The above-described bis(aminocarboxamide) was cyclized as follows: To 9.0 g. of the above product in 100 ml. of dry trichlorobenzene was added 7.6 g. (0.04 mole) of p-toluenesulfonic acid, and the mixture was refluxed under an atmosphere of nitrogen for about 27 hours, whereupon the maximum absorption peak at 36] nm. essentially disappeared. The mixture was allowed to cool, and the product which separated was EXAMPLE l8 When 3-amino-6-propyl-2-pyridinol is substituted for 3-amino-4-pyridinol in Example I hereinabove there is obtained 4,4'-stilbenebis(5-propyl-2-oxazolo[5,4- 5 blpyridine), having the structural formula Q (ll,

EXAMPLE 19 Following a procedure similar to that described above in Example I but using 3-amino-6-methyl-2- pyridinol instead of 3-amino-4-pyridinol there is ob- 2 tained 4,4-stilbenebis(5-methyl-2oxazolo[5,4-b]pyridine), having the structural formula 0 collected on a filter and was washed with trichloroben- C CH= zene and then methanol. The 4,4'-stilbenebis(2- imidazo[4,5-b]-pyridine) thus obtained, purified by O reprecipitation from aqueous alkaline methanol, re- CH3 mained unmelted at 300 C. and had the structural formula CH- N 40 CH N N H EXAMPLE 20 N Following a procedure similar to that described CH above in Example I except that 3-amino-5-bromo-4- pyridinol is used in place of 3-amino-4-pyridinol there is obtained 4,4'-stilbenebis(7-bromo-2-oxazolo[4,5- H c]pyridine), having the structural formula 5() EXAMPLE 22 Following a procedure similar to that described above in Example 2], but using 2,3-diamino6- chloropyridine instead of 2,3-diaminopyridine there is obtained 4,4'-stilbenebis(5-chloro-2-imidazo[4,5- blpyridine), having the structural formula cdOcib EXAMPLE 2i To l7.3 g. (0.05 mole) of dipotassium 4,4-stilbenedicarboxylate in 250 ml. of chlorobenzene was added dropwise and with stirring 21.3 g. (0. [8 mole) of thionyl chloride in 35 ml. of chlorobenzene. The mix C1 17 g l8 EXAMPLE 23 EXAMPLE 26 F ll ing a pr re i r to that described Following a procedure similar to that described above in Example except that above in Example 2| except that 2,3-diamino-4,5 6-

bromophridine is used in place of 2,3-diaminopyridine 5 i h l idi i d i place f 2 3-di i i there is Obtained dine there is obtained 4,4'-stilbenebis(5,6 7-trimethylimidazo[4,5-b]pyridine, having the structural formula 2 i id zo[4,5-b]-pyridine), having the structural formula \C CH- H ca g l Br 3 K is c CH N N 3 CH3 EXAMPLE 24 25 H H When 2,3-diamino-S-chloropyridine is substituted for 2,3-diaminopyridine in Example 21 hereinabove there is obtained 4,4'-stilbenebis(6-chloro-2- imidazo[4,5-b]pyridine), having the structural formula EXAMPLE 27 30 When 2,3-diamino-6-propylpyridine is substituted for 2,3-diaminopyridine in Example 2| hereinabove (31 N there is obtained 4,4'-stilbenebis(5-propyl-2- imidazo[4,5-b]pyridine), having the structural formula i CH: N N H C]. on I i N u n H CH C \N EXAMPLE 25 H Following a procedure similar to that described abovle in Example 2| but usi ng 2,3-di amino-5 6- EXAMPLE 28 gg f gz i Following a procedure similar to that described above in Example 21 but using 3,4-diaminopyridine instead of 2,3-diamin0pyridine there is obtained 4,4'-

stilbenebis(2-imidazo[4,5-c]pyridine) having the structural formula H- LII/Q Q6 01 a 3/ V N c1 1 v l N/ n \N a ti imidazo[4 5-b]pyridine), having the structural formula EXAMPLE 29 Following a procedure similar to'that described above in Example 21 except that 3,4-diamino-2- chloropyridine is used in place of 2,3-diaminopyridine there is obtained 4,4'-stilbenebis(4-chloro-2- imidazo[4,5-c]pyridine), having the structural formula EXAMPLE 30 When 3,4-diamino--bromopyridine is substituted for 2.3-diaminipyridine in Example 2l hereinabove there is obtained 4,4'-stilbenebis(7-bromo-2- imidazol4,5-c]pyridine), having the structural formula EXAMPLE 31 Following a procedure similar to that described above in Example 2l but using 3,4-diamino-2,5,6-trifluoropyridine instead of 2,3-diaminopyridine there is obtained 4,4'-stilbenebis(4,6,7-trifluoro-2- imidazol4,5-c]pyridine), having the structural formula 20 EXAMPLE 32 Following a procedure similar to that described above in Example 2l except that 3,4-diamino-2,6- dichloropyridine is used in place of 2.3-diaminopyridine there is obtained 4,4'-stilbenebis(4,6-dichloro-2- imidaz0[4,5-c]pyridine), having the structural formula \(LQCH- 1 EXAMPLE 33 When 3-amino-S-methyl-2-pyridinethiol is substituted for 3-amino-4-pyridinol in Example 1 hereinabove there is obtained 4,4'-stilbenebis(6-methyl-2- thiazolo[5,4-b]pyridine), having the structural formula CH C EXAMPLE 34 Following a procedure similar to that described above in Example 28 but using 2-methyl-4,4'-stilbenedicarboxylic acid instead of 4,4'-stilbenedicarboxylic acid there is obtained 2-methyl-4,4'-stilbenebis(2-oxazolo[5,4-b]pyridine), having the structural formula N\ CH- (mo CH3 EXAMPLE 35 Following a procedure similar to that described above in Example 2B except that 2,2'-dimethyl-4,4'- stilbenedicarboxylic acid is used in place of 4,4'-stilbenedicarboxylic acid there is obtained 2,2'-dimethyl- 4 4'stilbenebis(2-oxazolo[5,4-b1pyridine), having the structural formula c CH= N imidazol4 5-blpyridine) (Example 2l dissolved in ml. of 2-methoxyethano1 containing 1.6 g. of 50 percent aqueous sodium hydroxide solution is added l.l g. (0.02 mole) of acrylonitrile. The mixture is heated at approximately 50 for 2 hours, whereupon there is obtained 4,4'-stilbenebis[ l-(2-cyanoethyl )-2- imidazo[4,5-b]pyridine]t having the formula H2CH2-CN O f) on im ci-i cu EXAMPLE 37 Following the procedure of Example 36 using 4,4- stilbenebis(2-imidaz0[4,5-clpyridine) (Example 28) in place of 4,4-stilhenebis(2-imidazo[4,5-b]pyridine), there is obtained 4,4'-stilhenebis[l-(2-cyanoethyl)-2- imidazo[4,5-clpyridine], having the formula on c cn -cn -cu EXAMPLE 38 When 4,4'-stilbenebis[ l-(2-cyanoethyl )-2- imidazo[4,5-b]pyridine) (Example 36) is refluxed in excess dilute sodium hydroxide for 2 hours, acidified and filtered, there is obtained the hydrolysis product 4,4'-stilbenebis[ l-(2-carboxyethyl)-2-imidazo[4,5-

b] yridine] of the formula N c c EXAMPLE 39 Following the procedure given in Example 38, using 4,4'-stilbenebis[3-(2-cyanoethyl)-2-imidazo[4,5- clpyridinel (Example 37) in place of 4,4-stilbenebis[3-92cyanoethyl )2-imidazo[4,5-blpyridine] there is obtained 4' 4'-stilbenebis[ l-(2-carboxyethyl)- 2-imidazo[4,5-c]pyridine] of the formula l CH -CH -COOH EXAMPLE 4() Following the procedure of Example 36, using one molecular proportion of acrylonitrile for each molecular proportion of 4 4'-stilbenebis(2-imidazo[4,5- b]pyridine) there is obtained 4-[3-(2-cyanoethyl)-2- imidazol4,5-b]-pyridino]-4'-(2-imidazo[4,5- b]pyridino)stilhene of the formula Following the procedure of Example 36, using two molecular equivalents of dimethylsulfate instead of acrylonitrile, there is obtained 4,4'-stilbenebis(3-methyl-2-imidazo[4,5-blpyridine) of the formula N N a EXAMPLE 42 Following a procedure similar to that described above in Example 36, but using two molecular equivalents of allyl chloride instead of acrylonitrile there is obtained 4,4'-stilbenebis(3-allyl-2-imidazol4,5-b1pyridine) of the formula QIN/ CHCH=CH EXAMPLE 43 Following a procedure similar to that described above in Example 41 except that one molecular equiva lent of dimethyl sulfate is used in place of two molecu lar euivalents, there is obtaine i 4-(2-imidazo[4,5- b]pyridino)-4-(3methyl-2-imidaz 4,5-b]pyridino)- stilbene having the formula l c ii= EXAMPLE 44 When benzyl chloride is substituted for acrylonitrile in Example 36 hereinabove there is obtained 4,4stilbe'nebis(3-benzyl-2-imidazo[4,S-blpyridine) of the formula EXAMPLE 45 Following a procedure similar to that described above in Example 36 but using three molecular equivalents of 2,3-dihydroxypropyl chloride instead of acrylonitrile there is obtained 4-[3-(2.3-dihydroxypropyl)- 2-imidazo[4,5-b]pyridino]-4'-[3-(3-[2,3-dihydroxy propoxy]-2-hydroxypropyl)-2-imidazo[4,5- b]pyridine]stilbene of the formula C lH -CIDH-CH O CH -CH-CHEOH l cH -caoH-cr1 o1i EXAMPLE 46 When the reaction mixture containing the above compound (Example 45) is refluxed with another one molecular equivalent of 2,3-dihydroxypropyl chloride, there is obtained a produce consisting chiefly of 4.4- stilbenebis(3-[2-hydroxy-3-(2,3-dihydroxypropoxy)- propyl]-2-imidazo[4,5-b]pyridine) of the formula EXAMPLE 47 Following a procedure similar to that described above in Example 36, but using two molecular equivalents of ethyl acrylate instead of acrylonitrile there is obtained 4,4'-sti]benebis(3-[2-carbethoxyethyl1-2- imidazo[4,5-b]pyridine) of the formula JIH CH -COOC H EXAMPLE 4:;

Following a procedure similar to that described above in Example 36 except that 2 molecular equivalents of ethylene oxide are used in place of acrylonitrile there is obtained 4,4'-stilbenebis(3-[2-hydroxyethyl12- imidazo[4,5-]-pyridine) of the formula EXAMPLE 49 When two molecular equivalents of styrene oxide are substituted for ethylene oxide in Example 48 hereinabove there is obtained 4,4'-stilbenebis(3-[2-hydroxy- Z-phenylethyl]-2-imidazo[4,5-blpyridine) of the formula EXAMPLE 50 Following a procedure similar to that described above in Example 36. but using two molecular equivalents ofo-chlorobenzyl chloride instead of acrylonitrile there is obtained 4,4'-stilbenebis(3-lo-chlorobenzyll- HQcHfcOoce 5 55 2-imidazo[4,5-b]pyridine) of the formula EXAMPLE 51 Following a procedure similar to that described above in Example 36 except that one molecular equivalent of p-chlorostyrene oxide is used .in place of acrylo- 5 nitrile there is obtained 4-(2-imidazo[4,5-b]pyridino- 4'-( 3-[ 2-( 2-hydroxy-2-p-chlor0phenyl )ethyll-Z- imidazo[4 5-b]pyridine) of the formula The effectiveness of the optical brightening agents, prepared as above. when incorporated into polyethylene terephthalate melts, was tested as follows:

A solution of 4,4'-stilbenebis(2-oxazolo[5,4-b]pyridine) (Example 14A.) in dimethyl terephthalate was prepared by intermixing 0.04 gr. of the brightener with 10.00 gr. of dimethyl terephthalate and then-melting the two solids together. with continual stirring and under a carbon dioxide atmosphere, by immersing the container in a bath of diethyl phthalate maintained at 200 C. After about [5-20 minutes the fluid mixture was poured into a mortar and ground to a fine powder. The solid solution of brightener in diemthyl phthalate was incorporated into polyethylene terephthalate by blending H) g. of the brightener-dimethyl terephthalate powder with 19.0 g. of predried polyethylene terephthalate chips. The mixture was melted under a carbon dioxide atmosphere by immersing the container in a bath ofdiethyl phthalate which was heated to boiling (295-7 C. The melt was stirred for 5 minutes, and it then was removed from the bath and allowed to cool to room temperature continually under carbon dioxide. The polyethylene terephthalate casting was then broken up and ball milled with stoneware pellets in distilled water. The particles were dried and screened, and those passing through a 40 mesh screen were packed into a 5 cm. Petri dish. The color of the sample was then measured on a color difference meter (Hunterlab Model D-25, Hunter Associates Laboratory, McLean, Va.) in comparison with a standard magnesium oxide plate. These values were then compared with a blank sample prepared in the identical way except that the optical brightner was omitted. Following are the readings obtained in comparison with the standard magnesium oxide plate:

Hunterlab D-ZS Readings These results show that the shade of whiteness imparted to the polyethylene terephthalate was in the pink and blue range considered mostdesirable in the textile art. For the significance of the values recorded above, see. R. S. Hunter, Photoelectric Color Difference Meter. 1. Opt. Soc. Am.. 958 (1958) 30 wherein Py and Py are each a bivalent heterocyclic nucleus of the pyridine class in which the open bonds are on vicinal ring carbon atoms of said nucleus wherein each of the pyrido rings is otherwise unsubstituted or further substituted by a member of the class 35 consisting of halogen, lower alkoxy and lower alkyl; X

and X are each a member of the class consisting of O. S and NR, wherein R is H, lower alkyl. hydroxy-lower alkyl, hydroxyoxaalkyl of 3 to. l5 carbon atoms. phenyl-lower alkyl, cyano-lower alkyl, carboxy-lower alkyl. carbo-lower alkoxy-lower alkyl, phenyl-hydroxylower alkyl or lower alkenyl; and A is a bivalent 4.4- stilbene radical of the formula 2. A normally solid. fiber and film-forming polymeric material having incorporated therein about 0.005 to about 0.5 percent by weight of said polymeric material of a fluorescent compound according to claim 1 of the formula L a b Blank polyethylene terephthalate (PET) 98.6 +0.4 +0.9 PET containing 0.02 percent 4.4'-stilbenebis(2-oxazolol5,4-blpyridine) 99.0 +2.9 6.0

a c ca=c I N/ 3. A normally solid, fiber and film-forming polyester therein about 0.005 to about 0.5 percent by weight of material selected from the class consisting of polythe fluorescent compound according claim 1 4 4 (ethylene terephthalate) and poly(l,4-cyclohexsmbenebiqLomzolols 4 blpyridine) ylenedimethylene terephthalate) having incorporated 5 an m Page 1 of 2 UNITED STATES PATENT AND TRADEMARK OFFICE CERTIFICATE OF CORRECTION PATENT NO. 3, 928, 228 DATED December 25, 1975 |NVENTOR(S) Nathan N. Crounse St is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected shown below:

Abstract, oxazolopyridines,

line 1,

"oxazolopyridines-2" should read Column 1, line the structure should be labelled Formula I.

line '58, "thiazolo-[5, lb]" should read 4H, "chlorinetype" should read Column 2, line 20, "dihydroxypropoxy propyl, should read dihydroxypropoxy)propyl,

Column 3, line 2, "hexanesulfonyl," should read hexanesulfonyl;

Column 3, line 10, "napchylcarbamyl" should read naphthylcarbamyl Column 5, line 26, "(orthohydroxypridyl-" should read (orthohydroxypyridyD- after stilbenedicarboramide insert Column 5, line 27,

- N,N'-bis(orthomercaptopyridyl)- l, istilbenedicarboxamlde Column 6, line 23, "l582OCC." should read Page 2 of 2 UNITED STATES PATENT AND TRADEMARK OFFICE CERTIFICATE OF CORRECTION PATENT NO. 3, 928, 228

DATED December 23, 1975 INV ENTO (S) 1 Nathan N. Crounse It is certified that error appears in the ah0ve-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 6, line 36, "stilbenebis (2-" should read stilbenebis(2- Column '7, line 6, "hydroxyethoxy) ethoxy" should read hydroxyethoxy)ethoxy Column 7, line 20, "N,Ndia.lky1ated" should read N,N'-dialkylated "Nmm" should read N,N'-

Column 7, line 3 4,

Column 28, Claim 1, film-forming line 20, "filmforming" should read [SEAL] Arrest:

RUTH C. MASON Attesting Officer C. MARSHALL DANN Commissioner of Patents and Trademarks 

1. A NORMALLY SOLID, FIBER AND FILM-FORMING POLYMERIC MATERIAL HAVING INCORPORATED THEREIN ABOUT 0.005 TO ABOUT 0.5 PERCENT BY WEIGHT OF SAID POLYMERIC MATERIAL OF A FLUORESCENT COMPOUND O THE FORMULA
 1. A normally solid, fiber and filmforming polymeric material having incorporated therein about 0.005 to about 0.5 percent by weight of said polymeric material of a fluorescent compound of the formula
 2. A normally solid, fiber and film-forming polymeric material having incorporated therein about 0.005 to about 0.5 percent by weight of said polymeric material of a fluorescent compound according to claim 1 of the formula 